Multi purpose material with balanced properties
PA12-L 1600 SLS thermoplastic material is a mulit murpose material, with balanced properties, that produces strong druable parts with excellent surface finish.
Provides excellent chemical resistance to oils, greases, and alkalies. Ideal for complex assemblies, housings, enclosures, and watertight applications. Designed for production of functional parts across a variety of industries
| Feature | PA12-L 1600 | PA12-S 1550 | PA12-GFX 2550 |
|---|---|---|---|
| Bulk Density | 0.48 g/cm3 | 0.50 g/cm3 | 1.05 g/cm3 |
| Density Of Parts | 0.95 g/cm3 | 0.98 g/cm3 | 1.35 g/cm3 |
| Moisture Absorption | N.A | 0.50% (ASTM D570) | 0.33% (ASTM D570) |
| Melting Point | 183°C | 181-183°C | 181°C – 183°C |
| Heat Deflection 1.8 MPa | 83.5°C | 86°C | 116°C |
| Tensile Strength | 46 MPa | 44 MPa | 30 MPa |
| Tensile Modulus | 1602 MPa | 1550 MPa | 2550 MPa |
| Elongation @ break (XY) | 36% | 15% | 8% |
| Flexural Strength | 46.3 MPa | N.A | N.A |
| Flexural Modulus | 1300MPa | 1350 Mpa | 2275 MPa |
| Impact Strength (unnotched Izod) | 13.2 KJ/m2 | 68 KJ/m2 | 80 KJ/m2 |
| Shore Test (shore D) | NA | 68 Shore D | 77 Shore D |
| Upper facing processed & blasting, Surface Ra | NA | 7 µm | 8 µm |
| Upper facing after finishing, Surface Ra | NA | 7 µm | 1 µm |
| Testing Standard/Certification | GB/T | ISO | ISO |
| Resistivity Domain | Insulator | Insulator | Antistatic |